Aspecimen of a 4340 steel alloy with a plane strain fracture toughness of 54.8 mpa root m is exposed to a stress of 1030 mpa. will this specimen experience fracture if the largest surface crack is 0.5 mm (this is a) long? why or why not? assume that the parameter y has a value of 1.0.

It will not  experience fracture when it is exposed to a stress of 1030 MPa.

Explanation:

Given

Klc = 54.8 MPa √m

a = 0.5 mm = 0.5*10⁻³m

Y = 1.0

This problem asks us to determine whether or not the 4340 steel alloy specimen will fracture when exposed to a stress of 1030 MPa, given the values of KIc, Y, and the largest value of a in the material. This requires that we solve for σc from the following equation:

σc = KIc / (Y*√(π*a))

Thus

σc = 54.8 MPa √m / (1.0*√(π*0.5*10⁻³m))

⇒ σc = 1382.67 MPa > 1030 MPa

Therefore, the fracture will not occur because this specimen can handle a stress of 1382.67 MPa before experience fracture.