Engineering, 14.11.2019 03:31 hannahkharel2

The fatigue data for a ductile cast iron are given as follows: stress amplitude [mpa (ksi)] cycles to failure 248 (36.0) 1 × 105 236 (34.2) 3 × 105 224 (32.5) 1 × 106 213 (30.9) 3 × 106 201 (29.1) 1 × 107 193 (28.0) 3 × 107 193 (28.0) 1 × 108 193 (28.0) 3 × 108
(a) make an s–n plot (stress amplitude versus logarithm cycles to failure) using these data.
(b) what is the fatigue limit for this alloy?
(c) determine fatigue lifetimes at stress amplitudes of 230 mpa (33,500 psi) and 175 mpa (25,000 psi).
(d) estimate fatigue strengths at 2 × 105 and 6 × 106 cycles.

Answers: 1

Show answers

Another question on Engineering

Engineering, 04.07.2019 18:10

Water at 70°f and streams enter the mixing chamber at the same mass flow rate, determine the temperature and the quality of the exiting stream. 0 psia is heated in a chamber by mixing it with saturated water vapor at 20 psia. if both streams enters the mixing chamber at the same mass flow rate, determine the temperature and the quality of the existing system.

Answers: 2

Answer

Engineering, 04.07.2019 18:10

Adouble-strand no. 60 roller chain is used to transmit power between a 13-tooth driving sprocket rotating at 300 rev/min and a 52-tooth driven sprocket. a) what is the allowable horsepower of this drive? b) estimate the center-to-center distance if the chain length is 82 pitches. c) estimate the torque and bending force on the driving shaft by the chain if the actual horsepower transmitted is 30 percent less than the corrected (allowable) power.

Answers: 3

Answer

Engineering, 04.07.2019 18:20

Agas mixture consists of 8 kmol of h2 and 2 kmol of n2. determine the mass of each gas and the apparent gas constant of the mixture.

Answers: 3

Answer

Engineering, 04.07.2019 18:20

Atank with constant volume contains 2.27 kg of a mixture of water phases (liquid-vapor). in the initial state the temperature and the quality are 127 °c and 0.6, respectively. the mixture is heated until the temperature of 160 oc is reached. illustrate the process in a t-v diagram. then, determine (1) the mass of the vapor in kg at the initial state, (2) the final pressure in kpa.

Answers: 3

Answer

You know the right answer?

The fatigue data for a ductile cast iron are given as follows: stress amplitude [mpa (ksi)] cycles...

Questions